Machine foundation and method for preparing or repairing a machine foundation

ABSTRACT

The present invention is directed to a hollow form which is to be used as a machine foundation. The form is made of an aggregate filled thermosetting resin or a thermoplastic resin which are corrosion and chemical resistant materials free from fluid attack such as the liquids used in the machine, for example, in a pump either the lubricating fluids or the fluids being pumped. More particularly, the present invention is directed to a hollow form which may be used either to prepare a machine foundation or to repair a degraded slab or foundation and preferably is a single form. The preferred form has vertical walls and a single, top horizontal wall through which polymeric concrete can be poured to fill the form. An alternative form may be made of two pieces.

BACKGROUND OF THE INVENTION

This application is a continuation-in-part application of U.S. patent application Ser. No. 07/449,608 filed Dec. 11, 1989, ABND, entitled "MACHINE FOUNDATION AND METHOD FOR PREPARING OR REPAIRING A MACHINE FOUNDATION".

FIELD OF THE INVENTION

The present invention is directed to a form made of an aggregate filled thermosetting resin or a thermoplastic resin which is used to prepare or repair a machine foundation such as a foundation for a pump.

BACKGROUND OF THE INVENTION

Bases for equipment such as pumps have been pre-formed and designed for specific purposes such as to collect leaking liquids as illustrated by U.S. Pat. No. 2,916,233. Molds have been used to cast a reusable foundation for a pump jack as disclosed in U.S. Pat. No. 2,998,216.

Machine bases have used corrosion resistant materials such as disclosed in U.S. Pat. No. 4,632,346 and U.S. Pat. No. 4,731,915. In each of these patents epoxy materials are disclosed.

U.S. Pat. Nos. 4,670,208 and 4,826,127 disclose a method of manufacturing machine supports from acrylic concrete. These patent disclose various machine supports made from mixtures of aggregates and methacrylate monomer being poured into a prepared mold.

None of the prior art patents disclose a form made of an aggregate filled thermosetting resin or a thermoplastic resin which may be filled with a fortifying material to make a pump or other equipment foundation.

SUMMARY OF THE INVENTION

The present invention is directed to a hollow form which is to be used as a machine foundation. The form is made of an aggregate filled thermosetting resin or a thermoplastic resin which are corrosion and chemical resistant materials free from fluid attack such as the liquids in the machine, for example, in a pump the fluids being either the lubricating fluids or the fluids being pumped. More particularly, the present invention is directed to a hollow form which may be used either to prepare a machine foundation or to repair a degraded slab or foundation and preferably is a single form. The preferred form has vertical walls and a single, top horizontal wall through which polymeric concrete can be poured to fill the form. An alternative form may be made of two pieces.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a perspective view of the hollow form of the present invention positioned above a maze of reinforcement rods which together will create a machine foundation;

FIG. 2 is a perspective view of the hollow form of the present invention surrounding the maze of reinforcement rods and being filled with a setting, supportive material such as concrete;

FIG. 3 is a perspective view partly in cross-section of the finished machine foundation of the present invention;

FIG. 4 is a cross-sectional view of the finished machine foundation of the present invention;

FIG. 5 is another embodiment of the present invention wherein there are two pieces to the form used in repairing a machine foundation, one of the pieces surrounding a degraded concrete base to be repaired and the second piece of the form which is shown about to be positioned around the degraded base;

FIG. 6 is another embodiment of the present invention wherein the form is made of a themoplastic resin such as polyethylene sheets welded together and having a welded maze of polyethylene rods affixed to the form; and

FIG. 7 is a cross-sectional view of the form illustrated in FIG. 6.

BRIEF DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention is directed to forms which are used either in the preparation or the repair of machine foundations. Machines such as pumps and other equipment are usually bolted to concrete bases to secure the machines in place. The present invention is directed to preparing or repairing a machine foundations with a precast, injection molded or welded form. By making the form from a material which will not be attacked by the materials handled by the machines such as the liquid being pumped by a pump or by the lubricating fluids such as oils or greases, the life of the machine foundation may be extended and the foundation may be kept more easily in repair. A material which is free from fluid attack is meant herein as a material which is not absorbent, is corrosion resistant, will not react with the fluids in the machine and will retain structural integrity and preferably is either an aggregate filled thermosetting resin or a themosplastic resin. Further, by making the machine foundation from a material that is not subject to attack and has a surface that can be cleaned, overcomes the significant disadvantages of ordinary portland cement concretes. Ordinary concretes absorb the fluids, often times to substantial levels within the base or foundation. Ordinary concretes, in the case of leaks or spills, will require the removal of the contaminated concrete and in the case of hazardous materials pose a problem to any cleaning procedures for cleaning the base or foundation.

Referring now to FIG. 1, a hollow form 10 which is the preferred embodiment of the present invention for preparing a machine foundation is shown. The form 10 is precast when made of an aggregate filled thermosetting resin or is either injection molded or welded when made from a thermoplastic resin as will be described in more detail hereinafter. A specific example of a thermosetting resin is an epoxy based polymer concrete which utilizes select graded and blended aggregates suspended in a polyamine cured epoxy binder which is sold under the tradename "PC-1400" a product of Gulf Coast Paint Manufacturing in Mobile, Ala. Another example of a thermosetting resin which exhibits particular resistance to attack by chlorinated solvents and polar solvents is a novalac based polymer concrete which is sold under the tradename "EN-27", a product of Koch Corrosion Control in Houston, Tex. Still another example of a thermosetting resin which exhibits particular resistance to attack by organic acids as well as a wide range of inorganic acidic and alkaline materials is a vinyl ester based polymer concrete which is sold under the tradename "SEMSTONE 884", a product of Sentry Polmers in Freeport, Tex. These specific examples are but a few of the commercially available thermosetting resins made by these manufactures and by other manufacturers. The form 10 has vertical walls and in its preferred configuration is rectangular, has side walls 12 and end walls 14. The form 10 has a single horizontal wall namely upper wall 16. The form 10 has no lower horizontal wall and is hollow. The wall thicknesses may vary from 1/2 inch to 11/2 inches in thickness. A form 10 may be made in any number of configurations and sizes but for most pieces of equipment, primarily for pumps and smaller pieces of equipment, such machines will easily fit on a form 10 where the top horizontal wall 16 is rectangular and has dimensions for example of four (4) feet along the side walls 12 and two (2) feet along the end walls 14. The height of the form 10 is sufficient to encompass any reinforcing structure used to construct or repair the machine foundation. The height therefore may be as little as six inches or up to two (2) feet or greater. The horizontal or upper wall 16 of form 10 may have a plurality of bolt openings 18 and has at least one opening 20. As shown in FIG. 1, the form 10 has two openings 20, which are used to fill the form 10 as will be described in more detail hereinafter.

In preparing a new machine foundation, the ground is leveled and a concrete slab 40 may be poured. Foundations and bases for machines such as pumps and the like have used ordinary portland concrete. However, such concrete is porous and subject to attack by fluids in the machines or equipment. In preparing a new foundation according to the present invention, the outside surface of the slab 40 or the entire slab is a polymeric concrete to provide a surface which is washable and not absorbent to the fluids used or moved in the machines. The slab 40 is poured to support a reinforcement maze 30 of reinforcement rods. As shown in FIG. 1, slab 40 may be much larger than the horizontal dimensions of form 10 or may be essentially the same size or even smaller so that the form 10 surrounds the slab 40. Reinforcement rods 32 V which extend vertically are set by anchors 36 in the slab 40. These anchors 36 may be epoxy resins or mixtures which fill the drill holes or are mechanical wedges which anchor the reinforcement rods 32 V into the slab 40. As shown in FIG. 1, there are four, for purposes of illustration, vertically extending rods 32 V. To these vertical rods are attached the plurality of horizontal reinforcement rods 32 to form the reinforcement maze 30. The reinforcement rods 32 are connected together in the usual manner with tying wire 34 to form the maze 30. The maze 30 is constructed to provide strength and reinforcement to the material which will surround the maze 30 and provide the strength and support necessary for the machine. As an example of a complete foundation, tie down bolts 38 may be attached to the maze 30 for securing the machine to its foundation. As shown in FIG. 1, four tie down bolts 38 are supported by maze 30 and will bolt down a particular machine. The form 10 is lowered from the position shown in FIG. 1 to surround the maze 30 and permit the tie-down bolts 38 to pass through the respective openings 18 in form 10. The form 10 sits on the slab 40 with the tie-down bolts 38 extending above the horizontal upper wall 16.

The form is now in the position as shown in FIG. 2. A bead 13 of polymeric concrete is placed around the lower edge of form 10 to seal the form 10 to the slab 40. This bead 13 may be on the inside or outside of form 10. Since the machine foundation is constructed for a specific machine, the number and spacing of the tie down bolts 38 is predetermined or known for that specific machine. It is understood therefore that alternatively rather than the number and spacing of bolt openings 18 being part of producing the form 10, i.e. formed in the precast mold or injection molding operation, for example, the bolt openings 18 may be drilled into the horizontal wall 16. The use of a template having the spacing and number of openings 18 may be used. Then, instead of the tie down bolts 38 being affixed to the maze 30, the bolts 38 may be affixed to the form 10 by nuts 39. In this position (FIG. 2), a fortifying material 50 which will fill the form 10 is poured into openings 20 of the form 10 which surrounds the maze of reinforcement rods 32 and produces a reinforced concrete structure.

The fortifying material 50 used to fill the form 10 is a material which can be easily poured into the form 10 and surround the maze 30, which has fast setting properties, and which has very little shrinkage upon setting. The preferred fortifying materials are the polymer concretes as illustrated by the epoxy based polymer concretes which have all the desired properties. These epoxy based polymer concretes are commercially available from a number of sources. A specific example is epoxy based polymer concrete which utilizes select graded and blended aggregates suspended in a polyamine cured epoxy binder which is sold under the tradename "PC-1400" a product of Gulf Coast Paint Manufacturing in Mobile, Ala. One of the advantages of using a polymer concrete is that the concrete does not shrink upon setting and another is that the same material is used as the fortifying material as used in making the form 10. The compressive strength of these commercially available polymer concretes are within the range of 15,000 to 20,000 psi. The finished base is shown in FIG. 3.

The form 10 may be made or constructed of various thermosetting or thermoplastic materials. When thermosetting resins are the material of construction the form 10 is preferably precast, while when thermoplastic resins are used injection molding or welding are the preferred manner of construction. Thermosetting resins are such materials as the epoxy resins and the multicomponent epoxy resins, the styrene butadiene latexes, the acrylic latexes, the phenolic epoxy resins, the polyurethane resins, the polyester resins, the vinyl ester resins and the like. In using the thermosetting materials they are often used in combinations as well as being aggregate filled. By aggregate filled is meant that materials such as sand or rock such as silica or other mineral based solids or materials such as flint quartz, glass, fibers or other materials, such as a sheet of fiber glass or the like, are added to the thermosetting resins as fillers to increase strength. These aggregate filled thermosetting materials are already used as materials to top or restore concrete surfaces and are known material for such use. According to the present invention however, a form 10 as described hereinabove is produced by casting these materials in the shape desired to form or repair a machine foundation. On the other hand, if thermoplastic resins are employed to produce the form 10 then materials such as the polyolefins, specifically high density polyethylene or polypropylene, polyvinylchlorides or polycarbonates or even materials such as the polyesters, polyethersulfones, polyether ketones or polyether imides are used. These thermoplastic materials are preferably injection molded to produce the form 10.

There are features of the form 10 which are optional and two of which are shown in FIG. 4. Internal of wall 12 and wall 14 may be a plurality of angle pieces 15 which provides a surface for the fortifying material 50 to compress and retain the frame 10 on the slab 40. Moreover, the piece 15 provides for an integral structure between the form 10 and the material 50 which fills the form 10. A further detail is in regard to the opening 20. In a precast form 10 when made of a thermoplastic material, the opening 20 may have a tapered surface 22, tapered from a smaller diameter at the top surface to a larger diameter at the bottom surface of top wall 16. After the setting material 50 fills the form 10 up to the bottom surface of horizontal wall 16, a layer of aggregate filled thermosetting resin 17 which preferably is the same material used to precast the form 10, is used to close the opening 20. On the otherhand, the openings 20 of an injection molded form 10 may be formed for a cap, either a screw or snap cap, to close the opening. Further as shown in FIG. 4, nuts 59 may be used on the tie down bolts 38 above and below the wall 16. As shown in FIG. 1, after the form 10 is positioned a person can place a hand in the opening 20 and adjust the the tie down bolts 38 so that they are properly positioned on the lower surface of upper wall 16 before the setting material 50 is introduced into the form 10. The opening 20 is preferably large enough to insert a tool to make certain that the setting material 50 completely fills the form 10.

An optional feature of form 10 (not shown) is that when the form has a substantial dimension, for example is over six feet long that baffles or internal walls will provide small compartments to be filled rather than a single or the total hollow space. The baffled compartments are to insure that cavities or voids will not occur in the fortifying material 50 and that shrinkage is minimized.

Referring to FIG. 4, a cross-section of the finished machine foundation is shown. The form 10 is sitting on a slab 40 and provides the base for the machine. The maze 30 has vertical bars 32 V anchored in anchors 36 in the slab 40. The maze 30 is made up of a plurality of rebars or reinforcement rods 32. Inside the form 10 is fortifying material 50. The tie-down bolts 38 are secured to the upper horizontal wall 16 of the form 10 in the proper position for the machine.

FIGS. 1 to 4 not only depict a preferred embodiment of a hollow form 10 of the present invention, especially when the form is made from a thermosetting resin, which provides a fluid resistant machine base but also provides the basis for describing an easy method for preparing a machine foundation according to the present invention. The form 10, made from an aggregate filled thermosetting resin or thermoplastic resin, is brought to the site. The slab 40 is laid and the maze 30 erected. The form 10 is set in place. It should not be overlooked how easy these steps are as contrasted to attempting to construct in the field a foundation free from fluid attack. Most forms 10 of the present invention can be set in place by one man or no more than two simply by lifting and setting the form 10 in place. The form 10 optionally may be sealed with a bead 13 of the polymeric concrete used in making the form 10 or if the form 10 is a polyolefin such as high density polyethylene for example, the sealing material may be an epoxy based material. After making certain that the tie down bolts 38 are affixed to the upper surface of the form 10 and adjusted for the machine, fortifying material 50 is added to fill the form 10 to a point or level above the lowest angle pieces 15. Preferably, this amount of material 50 will compress the form 10 on the slab 40 and then is allowed to set so that leakage, if any, may be spotted and corrected before completely filling the form 10. The form 10 is then filled to the capacity of the hollow interior of the form 10. The opening 20 is closed either by using a layer of the aggregate filled thermosetting material when the form 10 is made of that material or by a cap if made from a thermoplastic material.

The presnt invention is illustrated by the following Example which includes the steps of making a form 10 from a thermosetting resin:

EXAMPLE I. Fabrication of 2 ft. wide×6 in Deep Precast Form of The Present Invention.

1. A two-piece male-female mold is constructed of 3/4 in. plywood which is reinforced with 2 in.×4 in. boards attached to the sides and ends of the mold.

2. A 10 in. circular plastic form is used to form a top opening.

3. The interior surface of the female piece of the mold and the exterior surface of the male piece of the mold are first coated with five coats of paste wax with drying between successive coats. A final coat of crystalline silicone dispersed in trichloroethane is applied and allowed to thoroughly dry.

4. A pourable polymer concrete material is prepared. A 100% solids cycloaliphatic amine cured phenolic epoxy resin manufactured by Gulf Coast Paint Manufacturing, Mobile, Ala. and sold under the tradename of "PC-1400" is mixed. An aggregate of flint quartz is added to the mixture of Base (Part A) and Hardener (Part B) which is mixed for approximately 1 to 2 minutes in a ratio of 1.5 to 2 parts Base to 1 part Hardener. The aggregate is slowly added until a uniform blend is achieved. The flint quartz has been chemically treated to develop an exceptionally strong bond with the resin.

5. The polymer concrete is poured into the bottom of the female mold to a depth of one inch with care being taken to maintain the circular plastic form in position to form an opening.

6. The male mold is then inserted and fitted with hold down braces to maintain wall thickness and prevent floating.

7. The polymer concrete mixture is then poured into the space between the male and female molds while mechanical vibrators insure void-free complete filling of the mold.

8. The completed assembly is allowed to cure over night before removal of the wooden mold.

II. Installation

1. An existing steel pump base and pump are removed from an existing concrete pump foundation.

2. Measurements are taken to determine the required elevation, longitude and latitude for setting a new pump base or specifically the precast form and replacing the pump.

3. Damaged and degraded areas of the existing concrete pump foundation are removed by a pneumatic chipping gun.

4. Existing pump anchor bolts may be lengthened and reused.

5. Measurements are taken of the bolt hole pattern and marked on top of the precast form.

6. Four holes are drilled through the top of the precast form using a 1/2 in. masonary drill bit.

7. The existing concrete pump foundation and the interior and exterior of the precast form are dry abrasive blasted to clean and remove surface contamination.

8. The precast hollow form is then placed over the existing pump foundation with the pump anchor bolts fitting through the pre-drilled holes in the top of the precast form.

9. The precast form is held in place by nuts securely fastened to the pump anchor bolts.

10. Polymer concrete is then prepared as was described in I-4 above and is poured into the formed hole in top of the precast form so that the space between the existing concrete pump foundation and the interior surface of the precast form is completely filled. Alternately, a non-shrinking, unexpanding cementatious grout may be used to fill the form.

11. The hold down nuts are removed after allowing curing for one hour.

12. The exterior of the precast form is then dry abrasive blasted and is top coated with a nominal 10-mil thick application of cycloaliphatic amine cured novolac epoxy manufactured by Gulf Coast Paint Manufacturing, Mobile, Ala. and sold under the tradename "PC-555".

13. The pump is then installed on top of the filled precast form which creates a chemical resistant foundation.

The forgoing example illustrates a form 10 of the present invention made of a thermosetting resin. Specifically, the example included an epoxy resin but other thermosetting resins or composite materials may be used.

Referring now to FIG. 5 another modification of the present invention may be employed to repair a cracked or degraded machine base. In this embodiment the hollow form is made from two forms having vertical walls made of either an aggregate filled thermosetting resin or thermoplastic resin which may be easily joined together to surround the existing degraded base. As depicted in FIG. 5 there are two vertical wall forms 60 and 64. Form 60 has a side wall 61 and an end wall 63. Comparable walls of form 64 are side wall 65 and end wall 67. Each of the forms 60 and 64 are provided with an easy attachment to each other such as tubular member 68 on end wall 63 and tubular member 69 on end wall 67. Through tubular members 68 and 69 a pin 70 is inserted to hold the two forms 60 and 64 together. The pin 70 has a large head 72 which will not fit through the tubular members 68 and 69 but secures form 60 and 64 in place around the degraded base. The precast forms 60 and 64 are placed around the slab one at a time and connected at both connecting edges. A sealing material such as an epoxy resin or suitable adhesive for the aggregate filled thermosetting resin or thermoplastic resin may be applied along the inner edges of form 60 and 62 where the two edges are connected by pins 70. It is understood that there are two connecting edges. Once the forms are in place the hollow form is filled with a setting material 50 similarly as form 10 substantially to the top of the form. As shown in FIG. 5, 82 depicts a fill level for the filling or pouring of fortifying material within the forms 60 and 64. The fortifying material is allowed to set and thereafter the form is then filled with a layer of the same material which was used in making the forms 60 and 64. When the fortifying material 50 is the same material used to make the forms 60 and 64 then the form is completely filled in one step. Again a completed foundation formed of a material free from fluid attack is thereby produced.

Another alternative of the two-piece form 10 is to have a single form having the side walls 12 and 14 and a second, seperate top piece 16. This alternative is especially advantageous for repairing a large foundation such as a pump base. This permits that the side wall form of form 10 be place around an existing or repaired maze and having clear access to filling the area between the maze and the side wall form. The single horizontal wall 16 or top is placed on the form 10, after the tie down bolts have been set and the form substanially filled with fortifying material 50, and a layer of uncured thermosetting resin is applied to fill the form. The top 16 is pulled down by using the tie down bolts so that the excess of uncured resin is forced up the openings around the tie down bolts as well as openings 20.

The above examples illustrate that the form 10 may be constructed in the field with pieces being pre-formed.

To construct a form 10 from a thermoplastic resin, specifically polyethylene, a simple and effective manner of making a form 10 is by welding sheets of the thermoplastic resin together. Referring to FIGS. 6 and 7, side walls 42 and 44 of a form 10 may be made from sheets of polyethylene. Polyethylene is heated above its melting point and applied as a weld bead 43 to the adjoining edges of the sheets of polyethylene, for example, between side sheet 42 and sheet 44, welding the two sheets 42 and 44 together. In a like manner sheet 44 is joined to top sheet 46 by a bead 45 of polyethylene and top sheet 16 is joined to side sheet 12 by weld bead 47 (not shown). With this construction of the form 10 using a thermoplastic resin such as polyethylene, a form 10 may be made which is relatively light in weight yet sturdy and completely free from fluid attack. Various modifications are possible to secure the thermoplastic form 10 to the slab 40 while the fortifying material 50 is poured into the form 10. For example, pieces of sheet polyethylene may be welded to the bottom of form 10 and bolted to the slab 40.

A feature of a form 10 made from thermoplastic sheets as illustrated in FIGS. 6 and 7 is that a maze, comparable to the maze 30, may be made internal of and a part of the form 10. Rods 48 of polyethylene or metal surrounded by polyethylene are cut and welded to the side walls either from side wall 42 to 42 or side wall 44 to 44. The weld beads 49 of polyethylene affix the rods 48 to the walls. The maze of rods 48 when surrounded by the fortifying material 50 which fills the hollow portion of the form 10 secures the form 10 to the slab 40. A fortifying material 50 such as a 3000 psi portland cement concrete, a material which is commonly used in pouring the slab 40, may be used to fill the form 10 and surround the rods 48 such as to assure that the form 10 is solidly affixed to the slab 40. A further example of fortifying material used with the thermoplastic resin form 10 and which has a slight expansion property is a product sold under the tredename "Supreme Expanding Grout", a product of Gifford-Hill in Houston, Tex. The advantage of a expanding fortifying material 50 in a polyethylene form 10 is that the form will be under tension and thus a stronger more solid foundation is produced.

When the foundation is a solid, uniform structure, the tendency for vibrations in the machine placed on the foundation is reduced. A foundation having the form of the present invention made from a thmosetting resin and filled with a fortifying material such as a polymer cement which adhere together provides the strongest structural foundation possible and the vibrations in the machine placed on the foundation are reduced. Thus, not only is the foundation being made of materials free from fluid attack but the foundation of the present invention reduces vibrations in the equipment placed on the foundation, thus extending the life of the equipment as well as the foundation. Forms of the present invention will last for far longer periods of time than coated or normal portland concrete machine foundations.

Various modifications of the specific dimensions as well as the shapes or form of the forms of the present invention are within the scope of the present invention. 

We claim:
 1. A corrosion resistant form for easily producing a machine foundation by surrounding reinforcement rods which extend vertically upward from a slab to secure the form to the slab and providing a flat surface for a machine including its machine base to be attached comprising:a precast hollow form made of an aggregate filled thermosetting resin; said hollow form having vertical walls of sufficient height and sufficiently spaced to surround the vertically extending reinforcement rods; said hollow form having a single horizontal wall extending from the top of said vertical walls of sufficient size to provide a horizontal, flat upper surface to attach said machine; and said horizontal wall having at least one opening of sufficient size to pour a fortifying material into said form and bolt openings for securing said machine.
 2. A form for a machine foundation according to claim 1 wherein said vertical walls are comprised of two side walls and two end walls.
 3. A form for a machine foundation according to claim 1 wherein said horizontal wall has at least two openings to receive a fortifying material.
 4. A form for a machine foundation according to claim 1 wherein said form is precast in at least two pieces.
 5. A corrosion resistant form for easily producing a machine foundation by surrounding reinforcement rods which extend vertically upward from a slab to secure the form to the slab and providing a flat surface for a machine including its machine base to be attached comprising:a preformed hollow form made of welded sheets of thermoplastic resin; said hollow form having vertical walls of sufficient height and sufficiently spaced to surround the vertically extending reinforcement rods; said hollow form having a single horizontal wall extending from the top of said vertical walls of sufficient size to provide a horizontal, flat upper surface to attach said machine; and said horizontal wall having at least one opening of sufficient size to pour a fortifying material into said form and bolt openings for securing said machine.
 6. A form for a machine foundation according to claim 5 wherein said vertical walls are comprised of two side walls and two end walls.
 7. A form for a machine foundation according to claim 5 wherein said sheets of thermoplastic resin are sheets of polyethylene.
 8. A form for a machine foundation according to claim 5 which further includes a maze of reinforcing rods welded to said vertical walls.
 9. A corrosion resistant machine foundation which has a single horizontal upper surface of sufficient size to attach a machine including its machine base comprising:vertically extending reinforcement rods which extend vertically upward from a slab; a precast hollow form of an aggregate filled thermosetting resin having vertical walls of sufficient height and sufficiently spaced to surround said vertically extending reinforcement rods; a horizontal wall made of an aggregate filled thermosetting resin extending from the top of said vertical walls and over said vertically extending reinforcement rods and providing said single horizontal upper surface for attaching said machine; and a fortifying material filling any voids between said vertically extending reinforcement rods, said vertical walls and said horizontal wall to secure said precast hollow form to the slab and provide a unified supporting foundation for said machine.
 10. A machine foundation according to claim 9 wherein said horizontal wall is a wall of said precast form.
 11. A machine foundation according to claim 9 wherein said horizontal wall is separately precast.
 12. A machine foundation according to claim 9 wherein said vertical walls are precast in more than one piece.
 13. A corrosion resistant machine foundation which has a single horizontal upper surface of sufficient size to attach a machine including its machine base comprising:vertically extending reinforcement rods which extend vertically upward from a slab; a preformed hollow form of a thermoplastic resin having vertical walls of sufficient height and sufficiently spaced to surround said vertically extending reinforcement rods; a horizontal wall made of a sheet of thermoplastic resin extending from the top of said vertical walls and over said vertically extending reinforcement rods and providing said single horizontal upper surface for attaching said machine; and a fortifying material filling any voids between said vertically extending reinforcement rods, said vertical walls and said horizontal wall to secure said preformed hollow form to the slab and provide a unified supporting foundation for said machine.
 14. A machine foundation according to claim 13 wherein said preformed hollow form is made from welded sheets.
 15. A foundation according to claim 13 which further includes a maze of reinforcing rods welded to said vertical walls of said preformed form. 